PALLUNA® 4700 Palladium Nickel Electrolyte

PALLUNA® 4700 Palladium Nickel Electrolyte

For hard and wear resistant coatings

PALLUNA® 4700 is a chloride-free, ammonia-reduced high-speed electrolyte for the deposition of a semi-bright to bright palladium-nickel alloy in reel-to-reel lines (selective dipping, jet plating, brush plating) and tabplaters.

Depending on the operating conditions, the electrolyte deposits alloy layers with approx. 80% of Pd. The alloy composition is largely independent of the current density.

The hard and wear-resistant layers are ductile, with low internal stresses and exhibit good corrosion resistance.

Actions

Electrolyte characteristics

Electrolyte type

Chloride-free ammoniacal

Metal content

20 g/l Pd, 15 g/l Ni

pH value

7.7

Operating temperature

40 °C

Current density range

up to 50 A/dm² in JetLab

Plating speed

up to 12 μm/min in JetLab

Anode material

Platinized titanium (e.g. PLATINODE®)

Coating characteristics

Coating

Palladium nickel

Purity

80 wt.% Pd, 20 wt.% Ni

Brightness

Semi-bright to bright

Hardness of deposit

approx. 550 HV kp/mm² (5mN load)

Density of the coating

ca. 10,8 g/cm³

Advantages

  • Chloride-free
  • pH and ammonia reduced
  • High deposition rate
  • Ductile coatings
  • Constant alloy composition

Applications

  • Industrial connectors (data and signal transmission)
  • IT connectors (e.g. USB-C)

Downloads

  • Produktblatt_PALLUNA_4700_EN.pdf
    Download

Your contact person

Markus Legeler

Markus Legeler

Manager Sales International
T: +49 7171 607 204
F: +49 7171 607 316
Email

Find a representative in your region

Get in touch