ARGUNA® C-100 Silver-Graphite Dispersion Electrolyte

ARGUNA® C-100 Silver-Graphite Dispersion Electrolyte

New standard for plug contacts in high-voltage applications

Our silver-graphite dispersion electrolyte ARGUNA® C-100 is specially developed for connector contacts used in high-voltage applications (e.g. high-power charging / HPC). A stable layer system with maximum charging performance without restrictions over the entire lifetime of the charging connectors is the result - and thus the new standard for the industry.

Graphite particles perfectly embedded in the silver layer achieve extraordinary abrasion resistance and thus the high reliability and durability of the plug contact required by the industry. This is made possible by a optimized graphite component which, embedded in the silver matrix, serves as a solid lubricant. In this way, abrasion on the entire contact zone during the mating process can be reduced to a negligible level.

ARGUNA® C-100 thus offers a contact layer on your connectors that is clearly superior to conventional coatings: more than 50,000 mating cycles* without adverse wear and therefore the best possible charging performance at all times without restriction - the new standard in this field.

Find out more about ARGUNA® C-100: New standard for plug contacts in high-power applications

Electrolyte characteristics

Electrolyte type

Alkaline-cyanide

Metal content

30 (25 - 35) g/l Ag

pH value

> 11

Operating temperature

18 - 25 °C

Current density range

1.5 (1.0 - 2.5) ASD

Plating speed

approx. 1 μm / 1.5 min at 1 ASD

Anode material

Silver

Coating characteristics

Coating

Silver-graphite dispersion surface

Purity

approx. 98 wt.% Ag

Colour of deposit

light grey to anthracite

Brightness

matt

Hardness of deposit

approx. 70-80 HV

Max. coating thickness

8 - 30 μm

Density of the coating

approx. 9.8 g/cm³

Advantages

  • Excellent electrical conductivity and even lower resistance than pure-silver
  • Outstanding tribological properties
  • Significantly reduced friction coefficients compared to pure and hard silver coatings
  • Consistent coating performance at elevated temperatures (>150°C)
  • Stable layering properties under humidity and dust and other exposed environmental conditions
  • Maintenance-free layer system over the entire service life the otherwise necessary lubrication is not required
  • Cross-compatibility with existing infrastructure matching the existing connector types in the field
  • Deposition of very thick layers possible

Applications

  • EV-Charging Connector
  • High voltage applications

Downloads

  • Produktblatt_ARGUNA_C-100_EN.pdf

 

 

* 50,000 mating cycles are the result of end-of-life tribometer tests under laboratory conditions